Engineering Plastics

 
Filter:
 
Material
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
MaterialMaterialColorAppearance
AS ZL 202Nylon 6WhiteAS ZL 202
AS ZL 202 MONylon 6 filled with molybdenum disulfide (MoS2)BlackAS ZL 202 MO
AS ZL 202 XNNylon 6 reinforced with nanoparticlesIvoryAS ZL 202 XN
AS ZL 250Nylon 6.6IvoryAS ZL 250
AS ZL 250 SWNylon 6.6BlackAS ZL 250 SW
AS ZL 250 HINylon 6.6 impact modifiedIvoryAS ZL 250 HI
AS ZL 250 PENylon 6.6 with a solid lubricantLight greenAS ZL 250 PE
AS ZL 250 GF30Nylon 6.6 + 30% glass fiberBlackAS ZL 250 GF30
AS ZL 600PE10PE 1000--
AS ZL 600PE5PE500--
AS ZL 600PEMPE MOL--
AS ZL 800Polypropylene--
AS ZL 900POM copolymerWhiteAS ZL 900
AS ZL 900 SWPOM-CBlackAS ZL 900 SW
AS ZL 900 PEPOM copolymer with a solid lubricantLight blueAS ZL 900 PE
AS ZL 900 ASAntistatic POM copolymerIvoryAS ZL 900 AS
AS ZL 900 XU ELSConductive POM copolymer filled with carbon nanotubesBlackAS ZL 900 XU ELS
AS ZL 900 XTPOM copolymer with a solid lubricantLight greyAS ZL 900 XT
AS ZL 900 XMDMetal detectable POM copolymerSapphire blueAS ZL 900 XMD
AS ZL 900 HPOM homopolymerWhiteAS ZL 900 H
AS ZL 900 H SWPOM-CBlackAS ZL 900 H SW
AS ZL 1100Cast nylon--
AS ZL 1100 OILCast nylon--
AS ZL 1115Cast nylon--
AS ZL 1100 MOCast nylon--
AS ZL 1200Cast nylon PA12 extruded--
AS ZL 1400PET copolymerWhiteAS ZL 1400
AS ZL 1400 SWPET-CBlackAS ZL 1400 SW
AS ZL 1400 HIPET homopolymer impact modifiedNaturalAS ZL 1400 HI
AS ZL 1400 TPET copolymer with a solid lubricantLight greyAS ZL 1400 T
AS ZL 1400 PBTPolybutylene terephthalateIvoryAS ZL 1400 PBT
AS ZL 1500PEEKBrownAS ZL 1500
AS ZL 1500 TPEEK filled with 10% carbon fiber, 10% grafite and 10% PTFEBlackAS ZL 1500 T
AS ZL 1500 XPEEKBrownAS ZL 1500 X
AS ZL 1500 GF30PEEK filled with 30% glass fiberGreyAS ZL 1500 GF30
AS ZL 1500 CA30PEEK filled with 30% carbon fiberAnthraciteAS ZL 1500 CA30
AS ZL 1500 C20Ceramic filled PEEKWhiteAS ZL 1500 C20
AS ZL 1600Polycarbonate--
AS ZL 1700Polyvinylidene fluoride--
AS ZL 1800Teflon--
AS ZL 1820Teflon--
AS ZL 1000PEIAmberAS ZL 1000
AS ZL 1000 GF30PEI filled with 30% glass fiberGreyAS ZL 1000 GF30
AS ZL 1900PolyphenylenesulfideBeigeAS ZL 1900
AS ZL 1900 GF40PPS filled with 40% glass fiberBeigeAS ZL 1900 GF40
AS ZL 2100PolyphenylsulfoneAmberAS ZL 2100
AS ZL PMMAAcrylic--
AS ZL PVC-UPVC-U--
Availability
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
AvailabilityRod diameterTube O.D.Sheet thicknessAvailablility
Unitmmmmmm
AS ZL 2026-31025-3100.3-100
AS ZL 202 MO6-20025-2802-100
AS ZL 202 XN6-150-8-100
AS ZL 2506-15025-2652-60
AS ZL 250 SW6-15025-2658-60
AS ZL 250 HI10-100-8-50
AS ZL 250 PE6-150-8-60
AS ZL 250 GF306-160-8-100
AS ZL 600PE10----
AS ZL 600PE5----
AS ZL 600PEM----
AS ZL 800---
AS ZL 9006-50025-5000.5-150
AS ZL 900 SW6-50025-5002-150
AS ZL 900 PE6-150-8-100
AS ZL 900 AS6-150-8-50
AS ZL 900 XU ELS6-150-8-50
AS ZL 900 XT6-150-8-50
AS ZL 900 XMD6-150-8-50
AS ZL 900 H6-150-8-100
AS ZL 900 H SW6-150-8-100
AS ZL 1100---
AS ZL 1100 OIL---
AS ZL 1115---
AS ZL 1100 MO---
AS ZL 1200---
AS ZL 14006-20025-2803-100
AS ZL 1400 SW6-15025-2808-60
AS ZL 1400 HI6-210-8-100
AS ZL 1400 T6-16025-2808-100
AS ZL 1400 PBT6-150-8-100
AS ZL 15005-20025-2808-60
AS ZL 1500 T6-16025-1608-60
AS ZL 1500 X5-20025-1608-60
AS ZL 1500 GF308-9025-16010-50
AS ZL 1500 CA308-90-10-50
AS ZL 1500 C208-90-10-50
AS ZL 1600---
AS ZL 1700---
AS ZL 1800---
AS ZL 1820---
AS ZL 100010-125-10-125
AS ZL 1000 GF3010-60-10-50
AS ZL 190010-60-10-50
AS ZL 1900 GF4010-50-10-50
AS ZL 210010-150-10-100
AS ZL PMMA---
AS ZL PVC-U---
Physical Properties
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
Physical PropertiesMass density (method D and E)Moisture absorption at 23 ºC and 50% RH (saturation)Water absorption at 23 ºC (saturation)
Test StandardISO 1183ISO 62ISO 62
Unitg/cm³%%
Condition of SpecimenDry
AS ZL 2021.13-1.153.0±0.48.0±0.5
AS ZL 202 MO1.1538
AS ZL 202 XN1.15--
AS ZL 2501.152.8±0.38.0±0.5
AS ZL 250 SW1.152.8±0.38.0±0.5
AS ZL 250 HI1.08-2.2
AS ZL 250 PE1.122.28.5
AS ZL 250 GF301.351.55.5
AS ZL 600PE10---
AS ZL 600PE5---
AS ZL 600PEM---
AS ZL 8000.9-0.91-0.03
AS ZL 9001.41-1.430.20.25
AS ZL 900 SW1.41-1.430.20.25
AS ZL 900 PE1.340.20.8
AS ZL 900 AS1.35--
AS ZL 900 XU ELS1.41--
AS ZL 900 XT1.440.20.6
AS ZL 900 XMD1.56<0.1-
AS ZL 900 H1.42-1.430.2-
AS ZL 900 H SW1.42-1.430.2-
AS ZL 11001.152.5-36-7
AS ZL 1100 OIL1.142.0-2.54.0-5.0
AS ZL 11151.132.5-36-7
AS ZL 1100 MO1.152.5-36-7
AS ZL 12001.030.91.4
AS ZL 14001.36~0.2311 b
AS ZL 1400 SW1.36~0.2311 b
AS ZL 1400 HI1.40.30.5
AS ZL 1400 T1.38~0.23~0.5
AS ZL 1400 PBT1.3-0.5
AS ZL 15001.320.10.5
AS ZL 1500 T1.480.06-
AS ZL 1500 X1.29-0.5
AS ZL 1500 GF301.510.110.4
AS ZL 1500 CA301.4-0.4
AS ZL 1500 C201.49-0.4
AS ZL 16001.2-0.35
AS ZL 17001.78--
AS ZL 18002.2-≤ 0.02
AS ZL 1820---
AS ZL 10001.270.71.25
AS ZL 1000 GF301.51--
AS ZL 19001.35-0.02
AS ZL 1900 GF401.64-0.02
AS ZL 21001.290.371.1
AS ZL PMMA1.19-0.3
AS ZL PVC-U1.44-0.2
Mechanical Properties
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
Mechanical PropertiesTensile strength at breakTensile strength at breakElongation at breakElongation at breakModulus of elasticity in tensionModulus of elasticity in tensionCharpy impact strength (+23 ºC)Charpy impact strength (-40 ºC)Charpy impact strength (notched)Charpy impact strength (notched)Hardness shore scale DTime yield limit σ 1/1000 (23 ºC/50% RH)Time yield limit σ 1/1000 (100 ºC)Apparent modulus E C/1000 2O (23 ºC/50% RH)
Test StandardISO 527ISO 527ISO 527ISO 527ISO 527ISO 527ISO 179/IeUISO 179/IeUISO 179/IeAISO 868ISO 899ISO 899ISO 899
UnitMPaMPa%%MPaMPakJ/m²kJ/m²kJ/m²kJ/m²MPaMPaMPa
Condition of SpecimenDryMoistDryMoistDryMoistDryDryDryMoistDryMoistDryMoist
AS ZL 202805050-10020030001500No breakNo break70-825.52.5230
AS ZL 202 MO75-25-2700-No break---80---
AS ZL 202 XN93-5-4200-----80---
AS ZL 25080605015032001600No breakNo break80-8063.5400
AS ZL 250 SW80605015032001600No breakNo break80-8063.5400
AS ZL 250 HI50-32-2000-No breakNo break8018----
AS ZL 250 PE65-11-2700-35-3-80---
AS ZL 250 GF30100-8-4800-20---85---
AS ZL 600PE10--------------
AS ZL 600PE5--------------
AS ZL 600PEM--------------
AS ZL 8001400-70---o.B.-7-72328-
AS ZL 90070-40-3000-No break80--8114--
AS ZL 900 SW70-40-3000-No break80--8114--
AS ZL 900 PE40-7-2200-17-2.5-77---
AS ZL 900 AS40-72-1380-No break---74---
AS ZL 900 XU ELS69-11-3600-80-3.4-80---
AS ZL 900 XT63-22-2800-----80---
AS ZL 900 XMD56-10-3200-90---81-60-
AS ZL 900 H72-40-3100-No break-11-84---
AS ZL 900 H SW72-40-3100-No break-11-84---
AS ZL 110088-9068-7010-4040-8039002500No break-2.5-35-1083.85Up to 5--
AS ZL 1100 OIL64-6651-5340-6070-10032002200No break-8-1012-2280-82Up to 4--
AS ZL 111578-8063-6540-100100-15031002000No break-3.5-4.56-1280-82Up to 4--
AS ZL 1100 MO90-9270-7210-3030-6041002800No break-2.2-2.84.5-8.583-85Up to 5--
AS ZL 120060-55-2200-No break--1575-8011--
AS ZL 140080-20-3200-82-14-8112--
AS ZL 1400 SW80-20-3200-82-14-8112--
AS ZL 1400 HI85-23-3250-59-3.9-84---
AS ZL 1400 T75-5-3230-23-10-81---
AS ZL 1400 PBT56->50-2600-No break-6-80---
AS ZL 150097-25-3600-No break---88---
AS ZL 1500 T141-2-9000-----85---
AS ZL 1500 X95-30-3500-No break-6.5-87---
AS ZL 1500 GF30155-2-11000-11.3-8.9-91---
AS ZL 1500 CA30240-1.7-25-45-6.4-----
AS ZL 1500 C2095-20-4100-No breakSection break7 break7 break----
AS ZL 160060-80---o.B.-40-75---
AS ZL 17001950-30---o.B.-12-78558-
AS ZL 1800400-700---------50-60---
AS ZL 1820--------------
AS ZL 1000105-60-3200-No break---86---
AS ZL 1000 GF30169---9300-----93---
AS ZL 190033---4200-No break-------
AS ZL 1900 GF40185-1.9-14000-45-------
AS ZL 210070->60-2300-No break---84---
AS ZL PMMA75-6---17-2-----
AS ZL PVC-U30-15---o.B.-4-82583-
Electrical Properties
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
Electrical PropertiesDielectric constant 1 MHzDielectric constantDissipation factor tan δ (1 MHz)Dissipation factor tan δDielectric strengthDielectric strengthVolume resistivityVolume resistivitySurface resistivity ROASurface resistivity ROAResistance to tracking (KA/KB method)Resistance to tracking (KC method)
Test StandardIEC 250IEC 250IEC 250IEC 250IEC 243IEC 243IEC 93IEC 93IEC 93IEC 93IEC 112IEC 112
UnitkV/mmkV/mmΩ·cmΩ·cmΩΩ
Condition of SpecimenDryMoistDryMoistDryMoistDryMoistDryMoistDry/MoistDry/Moist
AS ZL 2023.570.0230.31006010¹⁵10¹²10¹³10¹⁰KB>600KC>600
AS ZL 202 MO------>10¹²->10¹²---
AS ZL 202 XN------>10¹²-10¹¹---
AS ZL 2503.250.0260.21208010¹⁵10¹²10¹³10¹⁰KB>600KC>600
AS ZL 250 SW3.250.0260.21208010¹⁵10¹²10¹³10¹⁰KB>600KC>600
AS ZL 250 HI----31--->10¹²---
AS ZL 250 PE3.3-----10¹⁵-10¹³---
AS ZL 250 GF30----30->10¹²-10¹¹---
AS ZL 600PE10------------
AS ZL 600PE5------------
AS ZL 600PEM------------
AS ZL 800----52---10^14---
AS ZL 9003.8-0.024->20-10¹⁵---KB>600-
AS ZL 900 SW3.8-0.024->20-10¹⁵---KB>600-
AS ZL 900 PE4.4-0.003---10¹⁴-10¹⁴---
AS ZL 900 AS----14-10⁹-10¹⁰-10⁹-10¹⁰---
AS ZL 900 XU ELS------10⁴-10⁴---
AS ZL 900 XT3.7---33->10¹³->10¹³---
AS ZL 900 XMD-------->10¹²---
AS ZL 900 H------>10¹²->10¹²---
AS ZL 900 H SW------>10¹²->10¹²---
AS ZL 1100-----15-20-3-5x10¹²-1-3x10¹⁰--
AS ZL 1100 OIL-----15-20-3-5x10¹²-1-3x10¹⁰--
AS ZL 1115-----15-20-3-5x10¹²-1-3x10¹⁰--
AS ZL 1100 MO-----15-20-3-5x10¹²-1-3x10¹⁰--
AS ZL 1200-----50-1-3x10¹³-1-3x10¹⁵--
AS ZL 14003.3-0.02-50-10¹⁶---KA>450KC>600
AS ZL 1400 SW3.3-0.02-50-10¹⁶---KA>450KC>600
AS ZL 1400 HI-------->10¹³---
AS ZL 1400 T------------
AS ZL 1400 PBT3.2-----5x10¹³->10¹²---
AS ZL 15003.2-0.004-20-10¹⁶-----
AS ZL 1500 T------------
AS ZL 1500 X--0.005---10¹⁵-10¹⁵---
AS ZL 1500 GF303.2-0.004-20-10¹⁶-----
AS ZL 1500 CA30------------
AS ZL 1500 C20------------
AS ZL 1600----30---10^15---
AS ZL 1700----25---10^13---
AS ZL 1800------1.7-----
AS ZL 1820------------
AS ZL 1000------>10¹³->10¹³---
AS ZL 1000 GF303.4-0.0023--->10¹³->10¹⁵---
AS ZL 1900------>10¹²->10¹²---
AS ZL 1900 GF40------>10¹²->10¹²---
AS ZL 2100------>10¹³->10¹⁵---
AS ZL PMMA----30---10^14---
AS ZL PVC-U------0.8-----
Thermal Properties
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
Thermal PropertiesHeat disortion temperature (method A)Heat disortion temperature (method B)Melting point (method A)Max. service temperature for few hours operationTEP 5.000 hours (50% of tensile strength) ⁽¹⁾TEP 20.000 hours (50% of tensile strength) ⁽¹⁾Thermal coefficent of linear expansionThermal conductivity (method A)Specific heatFire performance (flameability according VDE)Fire performance (flameability of interior materials in passanger cars h>1 mm)Fire performance (flameability according UL standards, thickness of specimen 1.6 mm)
Test StandardISO 75ISO 75ISO 3146IEC 216IEC 216DIN 53752IEC 1006VDE 0304FMVSS 302UL 94
UnitºCºCºCºCºCºC1/K·10⁻⁵W/(K·m)J/(g·K)mm/min
Condition of SpecimenDryDryDryDryDryDryMoist
AS ZL 20255-75>160220≤18090757-100.231.711 b<100HB
AS ZL 202 MO--220--------HB
AS ZL 202 XN168-215--140-----HB
AS ZL 250100>200255≤20095807-100.231.711 b<100HB
AS ZL 250 SW100>200255≤20095807-100.231.711 b<100HB
AS ZL 250 HI64132263--------HB
AS ZL 250 PE120-----8.5----HB
AS ZL 250 GF30250250255250-1502-30.271.5--HB
AS ZL 600PE10------------
AS ZL 600PE5------------
AS ZL 600PEM------------
AS ZL 800------1.6-----
AS ZL 900110160164-168--10011-1.5BH 3-25 mm/min-HB
AS ZL 900 SW110160164-168--10011-1.5BH 3-25 mm/min-HB
AS ZL 900 PE120-----14----HB
AS ZL 900 AS--165---------
AS ZL 900 XU ELS--175---------
AS ZL 900 XT98-165140-100-----HB
AS ZL 900 XMD105--100--120-10---
AS ZL 900 H--178---10----HB
AS ZL 900 H SW--178---10----HB
AS ZL 1100------8x10⁻⁵-1.67--HB
AS ZL 1100 OIL------8x10⁻⁵-1.67--HB
AS ZL 1115------8x10⁻⁵-1.67--HB
AS ZL 1100 MO------8x10⁻⁵-1.67--HB
AS ZL 1200------10x10⁻⁵-1.7--HB
AS ZL 1400671652551601151006--11 b<100HB
AS ZL 1400 SW671652551601151006--11 b<100HB
AS ZL 1400 HI93.6189.5249160115100-----HB
AS ZL 1400 T---1601151006----HB
AS ZL 1400 PBT50135235---9-15----HB
AS ZL 1500152-340300260-4.70.25---V0
AS ZL 1500 T293-340300260-2.20.24---V0
AS ZL 1500 X1531763403002602345.8----V0
AS ZL 1500 GF30315-340---1.7----V0
AS ZL 1500 CA30336-343240--50.92---V0
AS ZL 1500 C20155210±340---0.45-8--V0
AS ZL 1600------------
AS ZL 1700------------
AS ZL 1800------------
AS ZL 1820------------
AS ZL 1000190200----5----V0
AS ZL 1000 GF30210212---------V0
AS ZL 190095115280---5.5----V0
AS ZL 1900 GF40200270280---3----V0
AS ZL 2100207-225---5.6----V0
AS ZL PMMA------------
AS ZL PVC-U------------
Friction Properties
 
Datasheet pdf available.
Datasheet pdf not available.
 
(1): Data of the resin only.
(2): Made by a pin/rotating disc test according DIN ISO 7148-2 under following conditions: Ra = 0.35 – 0.45 µm (steel disc), v = 0.3 m/s, p = 3 N/mm² and time T>16h.
 
Dry: Dried at 80 ⁰C and 1 mbar until weight is constant (moisture content less than 0.2%).
Moist: After storage in a standard atmosphere of 23 ⁰C and 50% relative humidity (DIN 50014) until saturation.
 
Friction PropertiesResistance to wear ⁽²⁾
Test StandardISO 7148-2
Unitµm/km
Condition of SpecimenDry
AS ZL 202-
AS ZL 202 MO-
AS ZL 202 XN-
AS ZL 250-
AS ZL 250 SW-
AS ZL 250 HI-
AS ZL 250 PE4.3
AS ZL 250 GF30-
AS ZL 600PE10-
AS ZL 600PE5-
AS ZL 600PEM-
AS ZL 800-
AS ZL 900-
AS ZL 900 SW-
AS ZL 900 PE2.1
AS ZL 900 AS-
AS ZL 900 XU ELS-
AS ZL 900 XT3
AS ZL 900 XMD-
AS ZL 900 H-
AS ZL 900 H SW-
AS ZL 1100-
AS ZL 1100 OIL-
AS ZL 1115-
AS ZL 1100 MO-
AS ZL 1200-
AS ZL 140022
AS ZL 1400 SW22
AS ZL 1400 HI1.9
AS ZL 1400 T1.1
AS ZL 1400 PBT-
AS ZL 1500-
AS ZL 1500 T-
AS ZL 1500 X-
AS ZL 1500 GF30-
AS ZL 1500 CA30-
AS ZL 1500 C20-
AS ZL 1600-
AS ZL 1700-
AS ZL 1800-
AS ZL 1820-
AS ZL 1000-
AS ZL 1000 GF30-
AS ZL 1900-
AS ZL 1900 GF40-
AS ZL 2100-
AS ZL PMMA-
AS ZL PVC-U-
 

The above values are provided for general purposes only and not meant to be a specific recommendation for any individual application. All values were determined under laboratory conditions. ASEC Kunststoffen B.V. is not directly neither indirectly responsible for any claim resulting from the use of any information provided in above values. ASEC Kunststoffen B.V. 2016 ©.